采用有机蒙脱土（OMMT）改性聚酰胺6（PA6）,并用熔融共混注塑成型的方法制备了PA6/OMMT复合材料,研究了复合材料的力学性能、耐热性能和摩擦磨损性能.结果表明,OMMT提高了复合材料的力学性能和耐热性,改善了PA6的摩擦磨损性能：OMMT含量为4 wt%时,复合材料的冲击强度和拉伸强度最大,比纯PA6分别提高了12.5%和10.9%;含量为2%时,维卡软化点温度达到最大,为212℃;含量分别为2 wt%和3 wt%时,摩擦因数和磨损率最低,比PA6分别降低了69.6%和47.3%.

The OMMT modified PA6 composites were prepared by means of melt blending and injection molding method. The mechanical properties, thermal property and tribological properties of the composites were researched. The results showed that all these properties of PA6 were improved by OMMT. The optimum value of impact strength and tensile strength of PA6/OMMT composite reached at 4 wt% loading of OMMT, which were 12.5% and 10.9% higher than neat PA6 respectively; the highest vicat softening temperature （212 ℃） came when OMMT content was 2wt%;while ...